Amathalente nobuchwepheshe yizici ezibalulekile ezisekela i-Alumina Cordierite Ceramic Ferrule ye-Stud Welding Ceramic base, ingxenye ye-ceramic okufanele idunyiswe kabanzi. Ukusetshenziswa okusabalele kumaCeramics omkhiqizo kuyisiza ukuthi izuze ukunakwa okuningi emakethe.
I-Liling xing tai ende ekhethekile ye-ceramic co., Ltd yenze intuthuko enkulu ekuthuthukisweni kwemigwaqo. I-Alumina Cordierite Ceramic Ferrule ye-Stud Welding Ceramic base, ingxenye ye-ceramic iwumkhiqizo wenkampani yethu owenziwe ubuchwepheshe besimanje. I-Alumina Cordierite Ceramic Ferrule ye-Stud Welding Ceramic base, ingxenye yeceramic enenani eligculisayo, ukusebenza okuhle kakhulu kanye nekhwalithi enhle kakhulu, izuze ukuqashelwa okubanzi kumakhasimende. I-Liling xing tai ende ekhethekile ye-ceramic co., ltd iyohlala inamathela kumgomo webhizinisi 'wekhwalithi kuqala, amakhasimende kuqala' futhi ilwela ukwakha inkampani eqhudelana nakakhulu futhi enekhono ehlose ikusasa elingcono nakakhulu.
Indawo Yomsuka: | I-Hunan, China | Uhlobo: | Izingxenye ze-Ceramic, i-alumina ceramic |
Isicelo: | Isakhiwo Ceramic | Okubalulekile: | I-Alumina Ceramic |
Inombolo Yemodeli: | I-XTL | I gama le-brand: | I-Xingtailong |
Umbala: | Emhlophe | Okuqukethwe kwe-Alumina: | 95% ~ 99% alumina, cordierite, Steatite |
Ubuso: | Okubushelelezi noma Okukhazimulayo | Amandla okucindezela okubandayo: | 450 MPa |
I-Thermal conductivity: | 25 W/m.k | Izinga lokushisa eliphezulu lesevisi: | 1900 degrees Celsius |
Amandla okufaka ugesi: | 20 KV/mm | Ukuminyana: | 3.95 g/cm3 |
I gama le-brand: | I-Xingtailong |
Ukusebenza For Industrial Ceramic
Into |
| Iyunithi | I-steatite ceramic | 95 Al2O3 | 96 Al2O3 |
Izici Zomzimba | Ukuminyana ngobuningi | g/cm3 | 2.7 | 3.6 | 3.6 |
Ukumuncwa kwamanzi | % | 0 | 0 | 0 | |
Izimpawu Zemishini | Amandla e-Flexural | Mpa | 145 | 320 | 340 |
Ubulukhuni Vickers | I-Gpa | 5.7 | 12.2 | 13.5 | |
I-Elastic module | I-Gpa | 120 | 280 | 320 | |
Isilinganiso sikaPoisson | - | 0.21 | 0.22 | 0.23 | |
Izici Zokushisa | Umugqa wokunweba i-coefficient | (20-5000C) 10-6/℃ | 7.9 | 7.1 | 7.2 |
I-Thermal conductivity | w/(m.k) | 2.5 | 16 | 24 | |
Ukushisa Okuthize | *10-3J/(kg*K) | 0.75 | 0.78 | 0.78 | |
Izici zikagesi | I-Dielectric constant (1MHZ) | - | 6.2 | 9 | 9.4 |
I-Dielectric loss angle | *10-4 | 18 | 15 | 5 | |
Amandla e-Dielectric | *106V/m | 18 | 12 | 15 |