Njengoko ukhuphiswano lwemarike lusiya lusiba luqilima, uLiling xing tai long special ceramic co.,ltd uye wanikela ingqalelo engakumbi kukubaluleka kwe-R&D yeemveliso ezintsha. Kwiinyanga ezimbalwa ezidlulileyo, sizinikele kuphuhliso lwemveliso entsha kwaye siphuhlise ngempumelelo umgangatho ophezulu wokuxhathisa ubushushu be-zirconia ceramic setter flat for eziko. I-Liling xing tai long special ceramic co.,ltd izinikele ekuqinisekiseni ukuba ufumana inkonzo yodidi oluphezulu, lonke ixesha. I-Liling xing tai long special ceramic co.,ltd ekumgangatho ophezulu kunye nodumo oluhle, iphumelele igama elihle kushishino.
Indawo yemvelaphi: | Hunan, China | Uhlobo: | Izinto zeCeramic Raw |
Isicelo: | Imveliso yeCeramic | Izinto: | Zirconia Ceramic |
Inombolo yoMfanekiso: | XTL | Igama lebrand: | Xing Tai Long |
Igama lemveliso: | umgangatho ophezulu ukumelana nobushushu i-zirconia ceramic setter flat for eziko | Umbala: | Mhlophe, isigqebelo |
Ubume: | yenziwe ngokwezifiso | Ubungakanani: | Umzobo wabaThengi |
Ukusetyenziswa: | Isinxibo esixhathisayo | Uphawu: | I-High Wear-resistance |
Ubuninzi: | 6.0 g/cm3 | Isatifikethi: | ISO9001 |
ubushushu bokusebenza: | 1600C |
Izalathisi zentsebenzo
Ukusebenza | ||||
Into | Iyunithi | 99 Al2O3 | Zirconia | |
Iimpawu zoMzimba | Unizi lolwapho kuyiwa khona | g/cm3 | 3.9 | 6.05 |
Ukufunxwa kwamanzi | % | 0 | 0 | |
Iimpawu zoomatshini | Mpa | 360 | 1000 | |
Amandla e-Flexural | ||||
Ubunzima Vickers | I-Gpa | 15.6 | 89 | |
Imodyuli ye-elastic | I-Gpa | 370 | 200 | |
Poisson’s umlinganiselo | - | 0.23 | 0.31 | |
Iimpawu zeThermal | I-coefficient yokwandiswa komgca | (20-5000C) 10-6/0C | 8 | 10 |
I-Thermal conductivity | w/(m.k) | 32 | 2.5 | |
Ubushushu obuthile | *10-3J/(kg*K) | 0.9 | 0.5 | |
Iimpawu zoMbane | I-Dielectric rhoqo (1MHZ) | - | 9.9 | N / A. |
I-angle yokulahlekelwa kwe-dielectric | *10-4 | 1 | N / A. | |
Amandla e-Dielectric | *106V/m | 15 | N / A. |