zirconia ceramic tube/pipe/rod/bar
Main production of fire assay crucible,Graphite crucible,Silicon carbide crucible.Also accept OEM and ODM.
Language
Main production of fire assay crucible,Graphite crucible,Silicon carbide crucible.Also accept OEM and ODM.
Having been through countless days and nights,Liling xing tai long special ceramic co.,ltd has successfully developed High Wearing Resistance Zirconia Porous Ceramic Tube/Pipe/Rod. It is bound to catch people's eyeballs in various fields. Technological innovation is the fundamental reason for Liling xing tai long special ceramic co.,ltd to achieve sustainable development. With a comprehensive understanding of the company management system, our employees can better realize their duties, which contributes to higher-efficiency manufacturing and more professional services. Our goal is to be a leading company in the global market.
| Place of Origin: | Hunan, China | Type: | Ceramic Raw Materials |
| Application: | Industrial Ceramic | Material: | Zirconia Ceramic |
| Model Number: | XTL-444 | Brand Name: | Xing Tai Long |
| Product name: | Zirconia Ceramic Tubes | Color: | White,irony |
| Shape: | round | Size: | Customer's Drawing |
| Usage: | Wear-resisting Material | Feature: | High Wear-resistance |
| Density: | 3.9 ~ 3.92 g/cm3 | Certificate: | ISO9001 |
| working temperature: | 1700C |
High Wearing Resistance Zirconia Porous Ceramic Tube/Pipe/Rod
Main performance index about ceramic tube:
| Item | unit | Alumina(1) | Alumina(2) | Zirconia | |||
| content | % | 95 | 99 | 99 | |||
| Density | g/cm3 | ≥3.6 | ≥3.8 | 5.89-6 | |||
| Water absorption | % | <0.01 | <0.01 | 0 | |||
| Hardness | HRA | ≥82 | ≥88 | 6-9 | |||
| Bending strength | MPA | 320 | 400 | 1100 | |||
| Dielectric constant | MHZ | 8.5 | 9.8 | 12 | |||
| Dielectric strength | KV/mm | 20 | 25 | - | |||
| Thermal expansion | X10-6/K | 5.0-8.3 | 5.4-8.3 | 9.6 | |||
| Volume Resistivity | Ω.cm20 | >10^15 | >10^14 | >10^12 | |||
| Maximum Use Temperature | °C | 1600 | 1750 | 900 | |||
| Thermal Conductivity ( at R.T. ) | W/(m.K) | 18-25 | 30 | 2.2 | |||
| Vickers Hardness | Gpa | 14 | 20 | 12 | |||
| Flexural Strength ( at R.T. ) | Mpa | 281 | 310 | 950 | |||
| Coefficient of | W/m °K | 2.5 | |||||
| thermal conductivity | |||||||