Main production of fire assay crucible,alumna ceramic,zirconia ceramic.Also accept OEM and ODM.
Language
Main production of fire assay crucible,alumna ceramic,zirconia ceramic.Also accept OEM and ODM.
After long-term exploration and hard work, Liling xing tai long special ceramic co.,ltd have launched Pakistan Germany Ceramic Silicon Carbide Graphite Crucibles For Melting Metals that lead the industry. High-end technologies are adopted to manufacture the product.When the product is manufactured and used in the field(s) of Graphite Crucible, its stability and advantages can be fully played out. Liling xing tai long special ceramic co.,ltd will keep pace with the tide and focus on improving technologies, thereby creating and manufacturing products that better suit the needs of customers. We aim to lead the market trends one day.
| Type: | Refractory, Ceramic Silicon Carbide Graphite Crucibles | Application: | For Metals Melting, For Furnace Of High Refractoriness & High Hardness |
| Height: | As required | Composition: | SiC |
| Top Diameter: | Min.72mm | Bottom Diameter: | Min.60mm |
| Place of Origin: | Hunan, China | Brand Name: | Xing Tai Long |
| Model Number: | XT | Model/Dimensions Available: | 5-1000Ml or customer request |
| Material: | Silicon Carbide & Graphite | Silicon Carbide Content: | 60-99% Max. |
| Color: | grey black | Using: | For Melting Metals |
| Refractoriness: | 1500~1700 | SHape: | block |
| welding parts: | firm and smooth |
The crucible is suitable for melting such metals as copper, gold ,silver, zinc, aluminium , lead .etc. Also represents capacity of molten copper in kiln.
Characteristic Of Products
High-temperature resistance, anti-oxidation, corrosion resisting, abrasion resistance, good conductivity and thermal efficiency. Mainly used in the various powder sintering and metal smelting in the fields of metallurgy, chemical industry and glass, and used as the dewatering and various grinding elements in paper making industry, which are broadly applied and are ideal ceramic substitutes.....
65-85% Content:
|
Item |
S65 |
S75 |
S85 |
|
SiC |
65% |
75% |
85% |
|
Fe2O3 |
1.5 |
1.2 |
1 |
|
Refractoriness |
≥1750°C |
≥1790°C |
≥1790°C |
|
Softening point under load at 0.2MPa |
≥1300°C |
≥1400°C |
≥1500°C |
90% Content:
|
Chemical composition SIC |
% |
≥ 90 |
|
|
Physics Property |
Max. service temperature |
°C |
1500 |
|
Density |
g/cm3 |
2.75 |
|
|
Porosity |
% |
≤12 |
|
|
2kg/ cm2 refractoriness under T2 |
Mpa °C |
>1700 |
|
|
Bending strength at room temp. |
Mpa |
≥45 |
|
|
Bending strength at 1200°C |
Mpa |
≥50 |
|
|
Compressive strength |
Mpa |
≥150 |
|
|
Thermal Conductivity at 1000°C |
W.(m.k)-1 |
≥ 12 |
|
Performance For Industrial Ceramic
Leave A Message
We are committed to producing the best quality products at the most competitive prices. Therefore, we sincerely invite all interested companies to contact us for more information.